IndexTLZ-NBS12TLZ-NBS22Whiteness %88-9088-90BaSO₄Content %8892Specific Gravity (g/cm³)4.04.20Particle Size D50 (μm)1-2 μm1-2 μmResidue (45 μm)0.005% max0.005% maxOil absorption (ml/100g)12 max12 maxPH7±17±1Moisture % ≤0.150.15Addition ratio10-40%15-40%
Contact Now
Synthesis Process：Produce the nano barium sulfate with carbonate solution and sulfuric acid andcoated with special technology.Application Areas：Transparent filler masterbatch Car PaintsIndexTLZ-PBS302BaSO₄ Content min%98% minMoisture max %0.15Water Soluble max %0.15lron Content5 ppmWhiteness %97 minBrightness (L Value )98-99%Oil Absorption10-20 g/cm³PH6.5-9.0Particle Size D500.3 μmResidue (45 μm)0.02% maxConductivity150 μs/cm
Contact Now
Product Features:1, The refractive index of this product is 1.64, same as most of the syntheticresin, and the particle size is nano grade, good transmittance of visible lightduring 390-780 nm, the optical property is very good.2, With special surface coated technology, low oil absorption, gooddistribution, good affinity with many kinds of resin, make the final productgood mechanical property, improve the filling rate, reduce the final cost.3, High L value, could guarantee the final product high glossy and goodbrightness.4, Without halogen, could guarantee the final product safety and cleanline
Contact Now
The Characteristics of TALENTS Precipitated Barium SulfateChemical synthesis used in the production of TLZ-PBS has endowed more outstanding performances. It becomes a good filler that has a high whiteness, low oil absorption, low wear index, and low bulk color.1. Excellent TLZ-PBS, acid and alkali resistance, good stability in water and resins improved its light resistance and weather resistance.2, We use advanced grinding technology and professional crystal form control in the production of TLZ-PBS.
Contact Now
Product Features:Particle size distribution is narrow.Less impurity.Excellent dispersibility.Natural Barium Sulfate Technical Data:Barium sulphate content (Baso4)%98Whiteness%≥96Water soluble content %≤0.15Fe Content % ≤0.0015Cl Content % ≤0.04PH Value6.5-7.5Oil absorption g/100g15-20Mean Particle Size (D50)1.2umResidue (45μm) %0.01Particle size less than 10μm %99Particle size less than 5μm %95Particle size less than 2μm %70Application Areas:Other Application Areas:Friction materialsGlass, ceramicRubberBattery
Contact Now
Synthesis Process：Produce the nano barium sulfate with carbonate solution and sulfuric acid andcoated with special technology.Application Areas：Transparent filler masterbatch Car PaintsIndexTLZ-PBS302BaSO₄ Content min%98% minMoisture max %0.15Water Soluble max %0.15lron Content5 ppmWhiteness %97 minBrightness (L Value )98-99%Oil Absorption10-20 g/cm³PH6.5-9.0Particle Size D500.3 μmResidue (45 μm)0.02% maxConductivity150 μs/cm
Contact Now
Synthesis Process：Produce the nano barium sulfate with carbonate solution and sulfuric acid andcoated with special technology.Application Areas：Transparent filler masterbatch Car PaintsIndexTLZ-PBS302BaSO₄ Content min%98% minMoisture max %0.15Water Soluble max %0.15lron Content5 ppmWhiteness %97 minBrightness (L Value )98-99%Oil Absorption10-20 g/cm³PH6.5-9.0Particle Size D500.3 μmResidue (45 μm)0.02% maxConductivity150 μs/cm
Contact Now
Barium hydroxide is mainly used in the petroleum industry additives and animal and plant oi refining, also used in the manufacture of barum salsynthetic rubber hardener, remove boiler scale, glass components, water softening and medicine, plastic Chemicalbook, glass, enamel and othelindustries. Barium hydroxide can also be used as a standard base for quantitaive analysis, determination of carbon dioxide content, etc. Bariumhydroxide should be stored in a sealed dry warehouse and not mixed with acids.Commercialy, barium hvdroxide is a precursor to other barum compounds.
Contact Now
IndexNational Standard GB/T2899-2008TLZ StandardBaSO₄ Content98.0% min98.5% minMoisture0.3 max0.15Water Soluble %0.3 max0.15lron %0.004 max5 ppmWhiteness %94 min97.5 minBrightness (L Value)-98-99%Oil Absorption10-30 g/cm³ 14-18 g/cm³PH6.5-9.07.0±1Particle Size D50-2-2.5 μmParticle Size D97-5 μm maxParticle Size D100-10 um maxResidue (45 μm)0.2% max0.05 maxConductivity-150 μs/cmSynthesis Process：By controlling the chemical reaction betweenbarium sulfide and sodium sulfate solutionsto produce barum sulfate in the originalparticle size.diversified applicationsThe hardness val
Contact Now
Application Areas：◆Oil drilling ◆Friction materials ◆Rubber ◆Radiation wallIndexTLZ-DB01TLZ-DB02AppearanceGranuleGranuleSpecial gravity ≥4.1 g/cm³4.2 g/cm³BaSO₄+ SrSO₄Content85%90%Hg ppm ≤1 ppm1 ppmCd ppm ≤3 ppm3 ppmAs ppm ≤40 ppm40 ppmPb ppm ≤1000 ppm1000 ppmSi0₂Content-3% maxFe₂O₃Content-3% maxCarbonates5000ppm max5000 ppm maxWater Soluble Alkaline Earth Metals As Calcium ≤250 mg/kg250 mg/kgMiosture2%2%Granule Size0-100 mm0-100 mm
Contact Now
Synthesis Process：Produce the nano barium sulfate with carbonate solution and sulfuric acid andcoated with special technology.Application Areas：Transparent filler masterbatch Car PaintsIndexTLZ-PBS302BaSO₄ Content min%98% minMoisture max %0.15Water Soluble max %0.15lron Content5 ppmWhiteness %97 minBrightness (L Value )98-99%Oil Absorption10-20 g/cm³PH6.5-9.0Particle Size D500.3 μmResidue (45 μm)0.02% maxConductivity150 μs/cm
Contact Now
IndexNational Standard GB/T2899-2008TLZ StandardBaSO₄ Content98.0% min98% minMoisture0.3 max0.15Water Soluble %0.3 max0.15lron %0.004 max5 ppmWhiteness %-97 minBrightness (L Value)10-30 g/cm³98-99%Oil Absorption6.5-9.014-18 g/cm³PH-7.0±1Particle Size D50-0.8±0.2 μmParticle Size D97-2-3 μmParticle Size D100-10 um maxResidue (45 μm)0.2% max0.05 maxConductivity-150 μs/cmSynthesis Process：By controlling the chemical reaction betweenbarium sulfide and sodium sulfate solutionsto produce barum sulfate in the originalparticle size.diversified applicationsThe hardness value of TLZ-PBS can reach Mo
Contact Now
Product Features:1, The refractive index of this product is 1.64, same as most of the syntheticresin, and the particle size is nano grade, good transmittance of visible lightduring 390-780 nm, the optical property is very good.2, With special surface coated technology, low oil absorption, gooddistribution, good affinity with many kinds of resin, make the final productgood mechanical property, improve the filling rate, reduce the final cost.3, High L value, could guarantee the final product high glossy and goodbrightness.4, Without halogen, could guarantee the final product safety and cleanline
Contact Now
ltem No.SpecificationUsageTLZ-HF10CaF₂≥ 40%Used to make aluminumfluoride and hydrofluoric acidUsed to make aluminumfluoride and hydrofluoric acidTLZ-HF20CaF₂≥60%Used to make aluminumfluoride and hydrofluoric acidUsed to make aluminumfluoride and hydrofluoric acidTLZ-HF30CaF₂≥80%Used as a fluxTLZ-HF40CaF₂≥97%The raw material ofthe Acid Grade Fluorite
Contact Now
Synthesis Process：Produce the nano barium sulfate with carbonate solution and sulfuric acid andcoated with special technology.Application Areas：Transparent filler masterbatch Car PaintsIndexTLZ-PBS302BaSO₄ Content min%98% minMoisture max %0.15Water Soluble max %0.15lron Content5 ppmWhiteness %97 minBrightness (L Value )98-99%Oil Absorption10-20 g/cm³PH6.5-9.0Particle Size D500.3 μmResidue (45 μm)0.02% maxConductivity150 μs/cm
Contact Now
Synthesis Process：Produce the nano barium sulfate with carbonate solution and sulfuric acid andcoated with special technology.Application Areas：Transparent filler masterbatch Car PaintsIndexTLZ-PBS302BaSO₄ Content min%98% minMoisture max %0.15Water Soluble max %0.15lron Content5 ppmWhiteness %97 minBrightness (L Value )98-99%Oil Absorption10-20 g/cm³PH6.5-9.0Particle Size D500.3 μmResidue (45 μm)0.02% maxConductivity150 μs/cm
Contact Now
Product Features:1, The refractive index of this product is 1.64, same as most of the syntheticresin, and the particle size is nano grade, good transmittance of visible lightduring 390-780 nm, the optical property is very good.2, With special surface coated technology, low oil absorption, gooddistribution, good affinity with many kinds of resin, make the final productgood mechanical property, improve the filling rate, reduce the final cost.3, High L value, could guarantee the final product high glossy and goodbrightness.4, Without halogen, could guarantee the final product safety and cleanline
Contact Now
Index & StandardAnalysis ResultTLZ-NBS11BaSO4 Content≥88%D50 Particle size5-7 μmWhiteness (dry)≥90Specific Gravity4.00 g/m3Oil Absorption≤7 ml /100 gPH Value7±1Moisture≤0.15%The Residue (325 mesh)noApplication Areas:1. Flat and textured powder coating2.Oil base and water base paints and powder coating3. Plastic (high gloss PP, ABS, Masterbatch and etc.)4. Rubber5. Glue
Contact Now
Index & StandardAnalysis ResultTLZ-NBS22BaSO4 Content≥92%D50 Particle size1.2-1.7 μmWhiteness (dry)≥92Specific Gravity4.20 g/m3Oil Absorption≤10 ml /100 gPH Value7±1Moisture≤0.15%The Residue (325 mesh)noApplication Areas :1. Flat and textured powder coating2. Oil base and water base paints and powder coating3.Plastic (high gloss PP, ABS, Masterbatch and etc.)4. Rubber5. Glue
Contact Now
Index & StandardAnalysis ResultTLZ-NBS12BaSO4 Content≥88%D50 Particle size1.2-1.7 μmWhiteness (dry)≥92Specific Gravity4.00 g/m3Oil Absorption≤10 ml /100 gPH Value7±1Moisture≤0.15%The Residue (325 mesh)noApplication Areas:1. Flat and textured powder coating2. Oil base and water base paints and powder coating3. Plastic (high gloss PP, ABS, Masterbatch and etc.)4. Rubber5. Glue
Contact Now
Index & StandardAnalysis ResultTLZ-NBS21BaSO4 Content≥92%D50 Particle size5-7 μmWhiteness (dry)≥90Specific Gravity4.20 g/m3Oil Absorption≤7 ml /100 gPH Value7±1Moisture≤0.15%The Residue (325 mesh)noApplication Areas:1. Flat and textured powder coating2. Oil base and water base paints and powder coating3.Plastic (high gloss PP, ABS, Masterbatch and etc.).4. Rubber5. Glue
Contact Now
Synthesis Process：Produce the nano barium sulfate with carbonate solution and sulfuric acid andcoated with special technology.Application Areas：Transparent filler masterbatch Car PaintsIndexTLZ-PBS302BaSO₄ Content min%98% minMoisture max %0.15Water Soluble max %0.15lron Content5 ppmWhiteness %97 minBrightness (L Value )98-99%Oil Absorption10-20 g/cm³PH6.5-9.0Particle Size D500.3 μmResidue (45 μm)0.02% maxConductivity150 μs/cm
Contact Now
Synthesis Process：Produce the nano barium sulfate with carbonate solution and sulfuric acid andcoated with special technology.Application Areas：Transparent filler masterbatch Car PaintsIndexTLZ-PBS302BaSO₄ Content min%98% minMoisture max %0.15Water Soluble max %0.15lron Content5 ppmWhiteness %97 minBrightness (L Value )98-99%Oil Absorption10-20 g/cm³PH6.5-9.0Particle Size D500.3 μmResidue (45 μm)0.02% maxConductivity150 μs/cm
Contact Now
Synthesis Process：Produce the nano barium sulfate with carbonate solution and sulfuric acid andcoated with special technology.Application Areas：Transparent filler masterbatch Car PaintsIndexTLZ-PBS302BaSO₄ Content min%98% minMoisture max %0.15Water Soluble max %0.15lron Content5 ppmWhiteness %97 minBrightness (L Value )98-99%Oil Absorption10-20 g/cm³PH6.5-9.0Particle Size D500.3 μmResidue (45 μm)0.02% maxConductivity150 μs/cm
Contact Now